Basic Info
Model NO.: HPM-P
Color: White Gray or Customized
Usage: Roofs & Underground Projects
Size: 1.2/1.5/2.0mm*20m*2.05m
Length: 20m
Width: 2.05m
Classification: Homogeneous; Fabric Backing; Polyester Reinforced
Certificates: ISO;SGS;D&B Duns No.530910769
Application: Roofing; Underground Engineering
Product Color: White;Grey or Cutomized
Product Name: Waterproofing PVC Building Material Membrane/PVC R
Trademark: Naijiu
Transport Package: Woven Bags
Specification: ISO; SGS
Origin: China
HS Code: 3921
| Quantity: | |
|---|---|
Product Description
Color: White Gray or Customized
Usage: Roofs & Underground Projects
Size: 1.2/1.5/2.0mm*20m*2.05m
Length: 20m
Width: 2.05m
Classification: Homogeneous; Fabric Backing; Polyester Reinforced
Certificates: ISO;SGS;D&B Duns No.530910769
Application: Roofing; Underground Engineering
Product Color: White;Grey or Cutomized
Product Name: Waterproofing PVC Building Material Membrane/PVC R
Trademark: Naijiu
Transport Package: Woven Bags
Specification: ISO; SGS
Origin: China
HS Code: 3921
Waterproofing PVC Building Material Membrane/pvc roofing membrane/pvc membrane
1. Products Introduction:
Polyvinyl Chloride(PVC) waterproof membrane is a new polymer waterproof membrane. The raw material is polyvinyl chloride resin,mixed with plasticizer,filler,antioxygen,ultravoilet absorber and other auxiliaries.
2. Specifications:
| Item | Specification |
| Length(m) | 20m (or customized) |
| Width (mm) | 2050 |
| Thickness(mm) | 1.2 / 1.5 / 2.0 |
3. Features:
1) Excellent aging resistance.
2) Root resistant penetration, specially used on planting roofings.
3) Welding installation. Joints are solid and environment friendly, no pollution.
4) High tensile strength, good elongation and dimensional stability.
5) Good plasticity, easy and suitable for details installation.
6) Fireproof. Fire extinguished out of the ignition resource.
7) Surface is smooth, no fading and dirty resistant.
8) Width is over 2m. Construction wastage is small, more economical.
4. Application:
PVC membrane applies special formula and its service life is much longer than other general waterproof membranes. Its excellent performance makes it be widely used in every field, such as artificial lake, steel construction roofing, accessible roofing,basement,planting roofing, and tunnels, and so on.
5.
Technical Data Sheet:
| HONGYUAN PVC Waterproof Membrane | Standard: GB12952-2011 | ||||||
| No. | Item | Unit | Value | ||||
| H | L | P | |||||
| 1 | Resin Thickness on Middle Mesh ≥ | mm | - | - | 0.4 | ||
| 2 | Tensile Properties | Max. Strength ≥ | N/cm | - | 120 | 250 | |
| Tensile Strength ≥ | Mpa | 10.0 | - | - | |||
| Elongation at Max. Strength ≥ | % | - | - | 15 | |||
| Breaking Elongation ≥ | % | 200 | 150 | - | |||
| 3 | Dimensional Stability after Heat Treatment ≤ | % | 2.0 | 1.0 | 0.5 | ||
| 4 | Foldability at Low Temperature | -25ºC No cracks | |||||
| 5 | Watertightness | 0.3Mpa, 2h No penetration | |||||
| 6 | Resistance to Impact | 0.5kg*m, No penetration | |||||
| 7 | Resistance to Static Loading* | - | - | 20kgs No penetration | |||
| 8 | Joint Peel Strength≥ | N/mm | 4.0 or membrane broken | 3.0 | |||
| 9 | Right Angle Tearing Strength≥ | N/mm | 50 | - | - | ||
| 10 | Trapezoid Tearing Strength≥ | N | - | 150 | 250 | ||
| 11 | Water Absorption (70ºC, 168h) | After immersing≤ | % | 4.0 | |||
| After drying≥ | % | -0.40 | |||||
| 12 | Aging in Hot Weather (80ºC) | Time | 672h | ||||
| Appearance | No bubbles, cracks, layering, sticky, holes | ||||||
| Max. Tensile Retention Rate ≥ | % | - | 85 | 85 | |||
| Tensile Strength Retention Rate ≥ | % | 85 | - | - | |||
| Elongation Retention Rate at Max. Tensile ≥ | % | - | - | 80 | |||
| Breaking elongation Retention rate≥ | % | 80 | 80 | - | |||
| Low Temperature Flexibility | -20ºC No cracks | ||||||
| 13 | Chemical resistance | Appearance | No bubbles, cracks, layering, sticky, holes | ||||
| Max. Tensile Retention Rate ≥ | % | - | 85 | 85 | |||
| Tensile Strength Retention Rate ≥ | % | 85 | - | - | |||
| Elongation Retention Rate at Max. Tensile ≥ | % | - | - | 80 | |||
| Breaking elongation Retention rate | % | 80 | 80 | - | |||
| Low Temperature Flexibility | -20ºC No cracks | ||||||
| 14 | Artificial aging* | Time | 1500h* | ||||
| Appearance | No bubbles, cracks, layering, sticky, holes | ||||||
| Max. Tensile Retention Rate ≥ | % | - | 85 | 85 | |||
| Tensile Strength Retention Rate ≥ | % | 85 | - | - | |||
| Elongation Retention Rate at Max. Tensile ≥ | % | - | - | 80 | |||
| Breaking elongation Retention rate | % | 80 | 80 | - | |||
| Low Temperature Flexibility | -20ºC No cracks | ||||||
| Remarks: *Resistance to static load is for PVC membranes used on roofing *The time of artificial aging of single-ply roofing membrane is 2500h. *Non-exposed membrane does not require determination of artificial aging. | |||||||